性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
泰伯磨耗 | H 18轮 | ASTM D-1044 | 20 | mg/1000rev |
24小时吸水率 | ASTM D-570 | 0.3 | % | |
比重 | ASTM D-792 | 1.28 | ||
泰伯磨耗 | CS-17轮 | ASTM D-1044 | 9 | mg/1000rev |
熔体流动速率 | ASTM D-1238 | 12.5 | g/10min | |
断裂伸长 | ASTM D-638 | 350 | % | |
初耐撕裂性能 | ASTM D-1004 | 253 | kn/m | |
硬度计硬度 | ASTM D-2240 | 82 | ||
埃佐冲击强度 | 23℃ | ASTM D-256 | 40 | J/m |
拉伸力(5%伸长) | ASTm D-638 | 27.6 | MPa | |
拉伸力(10%伸长) | ASTm D-638 | 30.3 | MPa | |
揉曲模 | 23℃ | ASTM D-790 | 1210 | MPa |
断裂拉伸力 | ASTM D-638 | 48.3 | MPa | |
热畸变温度 | @0.18MPa | ASTM D-648 | 55 | ℃ |
热畸变温度 | @0.5MPa | ASTM D-648 | 140 | ℃ |
维卡软化点 | ASTM D-1525 | 212 | ℃ | |
熔点 | ASTM D-3418 | 223 | ℃ | |
耐揉曲切口增长性能 | ASTM D-1052 | N/A |